Hot rolled EN10025-4 steel S355ML suppliers

Specification range of available steel EN10025-4 steel S355ML: thickness ≤ 650mm, width ≤ 4500mm, length ≤ 18000mm. Larger specifications of steel plates are also available as required. Our steel plates EN10025-4 steel S355ML can be supplied according to Chinese standard, American Standard AISI / ASME / ASTM, Japanese JIS, German standard DIN, French NF, British BS, European EN, international ISO and other standards. Heat treatment process: controlled rolling, normalizing, tempering, normalizing plus tempering, quenching and tempering, etc.

A514 gr.B steel coil chemical composition (melting analysis)%C: 0.12-0.21, Si: 0.20-0.35, Mn: 0.70-1.00, P max.: 0.035, S max.: 0.035, B max.: 0.005, Cr: 0.40-0.65, Mo: 0.15-0.25, V: 0.03-0.08, Ti: 0.01-0.03The mechanical properties in thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥, %: 18

The hot rolling method is to heat the EN10025-4 steel S355ML steel material to about 1000 ℃ ~ 1250 ℃ and use the rolling mill to roll it. The traditional hot rolling process is generally divided into the following two steps: the first step is to use the primary rolling mill or billet rolling mill to roll the ingot, billet or continuous casting billet into a certain shape and size of billet. This kind of EN10025-4 steel S355ML rolling process is usually called semi-finished product production, also called blank production.